EP Cores (6578070121)

Part Number: 6578070121
78 EP CORE SET
Dimensions
Inductive Components
Closed Magnetic Circuit
Printer Friendly Data Sheet
Check Stock
EP Cores

Part Number: 6578070121

78 EP CORE SET

EP designs reduce the effect of residual air gap upon the effective permeability of the core, hence they minimize coil volume for a given inductance. EP cores also provide a high degree of isolation from adjacent components and are advantageously used in low power devices, matching and broadband transformers.

•EP cores can be supplied with the center post gapped to a mechanical dimension or an ALvalue.

Weight indicates is per pair or set.

Weight: 0.7 (g)

Dimmmmm tolnominal inchinch misc.
A9.2± 0.200.362_
B3.7± 0.200.146_
C6.4± 0.200.252_
D2.7± 0.200.106_
E7.2min0.283min
F3.3± 0.100.13_
K1.8min0.071_

Chart Legend
Σl/A  :  Core Constant,    le :  Effective Path Length,    Ae :  Effective Cross-Sectional Area,    Ve :  Effective Core Volume
AL :  Inductance Factor  
Explanation of Part Numbers: Digits 1 & 2 = product class and 3 & 4 = material grade.

Electrical Properties
AL(nH)990 ±25%
Ae(cm2)0.103
Σl/A(cm-1)14.4
le(cm)1.48
Ve(cm3)0.152
Amin(cm2)0.085

AL value is measured at 1 kHz, B < 10 gauss

A MnZn ferrite specifically designed for power applications for frequencies up to 200 kHz and low loss inductive applications to 500 kHz.

Available in 78 material:

RFID Rods

Toroids

Mated Parts

78 Material Characteristics
Property Unit Symbol Value
Initial Permeability @ B < 10 gauss µi 2300
Flux Density @ Field Strength Gauss
Oersted
B
H
4800
5
Residual Flux Density Gauss Br 1500
Coercive Force Oersted Hc 0.20
Loss Factor @ Frequency 10 -6
MHz
Tan δ/ µi 4.5
0.1
Temperature Coefficient of Initial Permeability (20 -70°C) %/°C 1.0
Curie Temperature °C Tc >200
Resistivity ohm-cm ρ 200

**** Characteristic curves are measured on standard Toroids (18/10/6 mm)  at 25°C and 10 kHz unless otherwise indicated. Impedance characteristics are measured on standard shield beads (3.5/1.3/6.0 mm) unless otherwise indicated.

Ferrite Material Constants

Specific Heat
0.25 cal/g/°C
Thermal Conductivity
3.5 - 4.5 mW/cm-°C
Coefficient of Linear Expansion
8 - 10x10-6/°C
Tensile Strength
4.9 kgf/mm2
Compressive Strength
42 kgf/mm2
Young's Modulus
15x103 kgf/mm2
Hardness (Knoop)
650
Specific Gravity
≈4.7 g/cm3
The above quoted properties are typical for Fair-Rite MnZn and NiZn ferrites.