Bobbins (9877000104)

Part Number: 9877000104
77 BOBBIN RECTANGULAR
Power Applications
Inductive Components
Open Magnetic Circuit
Printer Friendly Data Sheet
Check Stock
Bobbins

Part Number: 9877000104

77 BOBBIN RECTANGULAR

Explanation of Part Numbers:
– Digits 1 & 2 = Product Class
– Digits 3 & 4 = Material Grade
•– Last digit 8 = Coated Bobbin

Bobbins are an economical and well-proven core design for many applications where relatively low but stable inductance values are required.

For higher frequency designs, use small bobbins in 43 material.
•
For power applications, bobbins in 77 material are specified for AL and dc bias limits.

Bobbins in Figures 2-5 can be supplied with a uniform thermo-set plastic coating which can withstand a minimum breakdown of 500Vrms. This coating will change the dimensions a maximum of 0.5 mm (0.020″). The last digit of the thermo-set plastic coated part is an “8”.

•For any bobbin requirement not listed in the catalog, please contact our customer service group for availability and pricing. 

Weight: 3 (g)

Dimmmmm tolnominal inchinch misc.
A8.05±0.200.317_
B19±0.400.75_
D12.7±0.250.5_
F5.55+0.250.225_
G2.7+0.250.111_
H8.05±0.200.317_

Chart Legend
AL :  Inductance Factor   ,   Nl : Value of dc Ampere-turns,    AW:Winding Area,
N/AWG : Number of Turns/Wire Size for Test Coil

Electrical Properties
AL(nH)39 ±10%
AL min. @ Nl (At)33 - 125
N/AWG36/24
Aw(cm2)0.33

Bobbins are tested for AL value at 1kHz < 10 gauss.

A MnZn ferrite for use in a wide range of high and low flux density inductive designs for frequencies up to 100 kHz.

Available in 77 material:

Pot Cores

E&I Cores

U Cores

Rods

Toroids

Bobbins

77 Material Characteristics
Property Unit Symbol Value
Initial Permeability @ B < 10 gauss µi 2000
Flux Density @ Field Strength Gauss
Oersted
B
H
5100
5
Residual Flux Density Gauss Br 1800
Coercive Force Oersted Hc 0.25
Loss Factor @ Frequency 10 -6
MHz
Tan δ/ µi 15
0.1
Temperature Coefficient of Initial Permeability (20 -70°C) %/°C 0.7
Curie Temperature °C Tc >200
Resistivity ohm-cm ρ 100

**** Characteristic curves are measured on standard Toroids (18/10/6 mm)  at 25°C and 10 kHz unless otherwise indicated. Impedance characteristics are measured on standard shield beads (3.5/1.3/6.0 mm) unless otherwise indicated.

Ferrite Material Constants

Specific Heat
0.25 cal/g/°C
Thermal Conductivity
3.5 - 4.5 mW/cm-°C
Coefficient of Linear Expansion
8 - 10x10-6/°C
Tensile Strength
4.9 kgf/mm2
Compressive Strength
42 kgf/mm2
Young's Modulus
15x103 kgf/mm2
Hardness (Knoop)
650
Specific Gravity
≈4.7 g/cm3
The above quoted properties are typical for Fair-Rite MnZn and NiZn ferrites.


Printer Friendly Data Sheet - Download as pdf file